Product Details:
Material Grade | Monel 400 |
Material | Monel |
Density | 8.80 g/cm3 / 0.318 lb/in3 |
Melting Point | 2370-2460 Deg F / 1300-1350 Deg C |
Standards | ASTM (B 127),ASME (SB 127) |
Width | 100 mm - 2000 mm |
Thickness | 4mm - 50 mm |
Length | 1000 mm - 6000 mm |
Tension | 26.0 |
Compression | 26.0 |
Torsion | 9.5 |
Poisson's Ratio | 0.32 |
Curie Temperature | 70-120 Deg F / 21-49 Deg C |
Nickel | Carbon | Manganese | Iron | Sulfur | Silicon | Copper | |
Min | 63 | - | - | - | - | - | - |
Max | - | 0.3 | 2 | 2.5 | 0.024 | 0.5 | 28.0-34.0 |
Product Details:
Material | Monel |
Thickness | 4mm - 50 mm |
Density | 8.80 g/cm3 / 0.318 lb/in3 |
Melting Point | 2370-2460 Deg F / 1300-1350 Deg C |
Standards | ASTM (B 127), ASME (SB 127) |
Width | 100 mm - 2000 mm |
Length | 1000 mm - 6000 mm |
Tension | 26.0 |
Compression | 26.0 |
Torsion | 9.5 |
Poisson's Ratio | 0.32 |
Curie Temperature | 70-120 Deg F / 21-49 Deg C |
Nickel | Carbon | Manganese | Iron | Sulfur | Silicon | Copper | |
Min | 63 | - | - | - | - | - | - |
Max | - | 0.3 | 2 | 2.5 | 0.024 | 0.5 | 28.0-34.0 |