Product Details:
Minimum Order Quantity | 20 Kilogram |
Density | 0.321 lb/in3 / 8.89 g/cm3 |
Melting Point | 2415-2500 Degree F / 1325-1370 Degree C |
Thickness | 4 - 50 mm |
Material | Hastelloy |
Standard | ASTM (B-575), ASME (SB-575) |
Grade | C276 |
Young Modulus | 29.8 / 208 (103 ksi / GPa) |
Thermal Conductivity | 67.9 Btu in/(h ft2 Deg F) / 9.8 W/m Deg C |
INCONEL alloy C-276 (UNS N10276/W.Nr. 2.4819) is known for its corrosion resistance in a wide range of aggressive media. The high molybdenum content imparts resistance to localized corrosion such as pitting. The low carbon minimizes carbide precipitation during welding to maintain resistance to intergranular attack in heat-affected zones of welded joints.
Alloy C-276 is a nickel-chrome-molybdenum alloy with tungsten. It is characterized by:
Chemical Composition:
Ni | Cr | Fe | C | Mn | Si | W | Mo | Co | V | P | S | |
Min | 51 | 15 | 4 | 3 | 15 | |||||||
Max | 63 | 17 | 7 | 0 | 1 | 0 | 5 | 17 | 3 | 0 | 0 | 0 |
Product Details:
Minimum Order Quantity | 10 Kg |
Material | Hastelloy |
Usage/Application | Chemical Handling |
Application | Gas Handling |
Shape | Round |
Range | 6 NB To 600 NB IN SCH 5S,10S,10,20,40S,40,STD,60,80S,80,XS,100,120,140,160 & XXS |
Density | 0.321 lb/in3 / 8.89 g/cm3 |
Melting Point | 2415-2500 Degree F / 1325-1370 Degree C |
Young Modulus | 29.8 / 208 (103 ksi / GPa) |
Chemical Composition:
Ni | Cr | Fe | C | Mn | Si | W | Mo | Co | V | P | S | |
Min | 51 | 15 | 4 | 3 | 15 | |||||||
Max | 63 | 17 | 7 | 0 | 1 | 0 | 5 | 17 | 3 | 0 | 0 | 0 |
Product Details:
Material | Hastelloy |
Grade | Hastelloy C276 |
Shape | Round |
Range | 6 NB TO 600 NB IN SCH 5S,10S,10,20,40S,40,STD,60,80S,80,XS,100,120,140,160 & XXS |
Density | 0.321 lb/in3 / 8.89 g/cm3 |
Melting Point | 2415-2500 Degree F / 1325-1370 Degree C |
Young Modulus | 29.8 / 208 (103 ksi / GPa) |
Thermal Conductivity | 67.9 Btu in/(h ft2 Deg F) / 9.8 W/m Deg C |
Ni | Cr | Fe | C | Mn | Si | W | Mo | Co | V | P | S | |
Min | 51 | 15 | 4 | 3 | 15 | |||||||
Max | 63 | 17 | 7 | 0 | 1 | 0 | 5 | 17 | 3 | 0 | 0 | 0 |